１００℃で１５時間反応を行い、エポキシ当量が１８，０００ｇ／ｅｑ．、酸

１００℃で１５時間反応を行い、エポキシ当量が１８，０００ｇ／ｅｑ．、酸価が０．４ｍｇＫＯＨ／ｇ、溶液粘度（酢酸ブチル不揮発分８０質量溶液)１．８Ｐａ・ｓである重合性不飽和基含有樹脂（１）を得た。得られた重合性不飽和基含有樹脂（１）の１３Ｃ－ＮＭＲを測定に基づく各末端構造部位の存在割合を表１に示した。

結果 (英語) 1:

100 ° C at 15 h and the reaction the epoxy equivalent 18000 g/eq. The acid value is 0. 4mgKOH/g, viscosity (acetate butyl non-volatile: 80 weight solution) 1. Got 8 Pa-s in polymerizable unsaturated-containing resin (1). Table 1 shows the ratio of each terminal structure based on measurements obtained polymerization based on content of unsaturated resin (1) 13 c-NMR.

結果 (英語) 2:

Perform 15 hours of the reaction at 100 ℃, epoxy equivalent 18,000g / eq. Acid value was obtained 0.4mgKOH / g, the solution viscosity (butyl acetate nonvolatile content 80 mass solution) is 1.8Pa · s polymerizable unsaturated group-containing resin (1). The proportion of the terminal structure parts based the 13C-NMR in the measurement of the resultant polymerizable unsaturated group-containing resin (1) to I shown in Table 1.

結果 (英語) 3:

The reaction is carried out at 100 ℃ for 15 hours, 18, 000 epoxy equivalent ， g and the acid value of 0.4 mgKOH EQ / g, the solution viscosity of butyl acetate solution (nonvolatile content of 80% by weight of resin containing a polymerizable unsaturated group in 1.8 Pa s (1) is obtained. Unsaturated group-containing polymerizable resin obtained: (1) the existence of each end portion 13 -- Based on structural C NMR measuring proportion shown in Table 1.